PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|---|
60±2 | 29000±5000 | 5.0±0.5 | 14 | PVOH | Fast Setting | |
50±1 | 60000±10000 | 4.5±0.5 | 14 | PVOH | Standard PVAc | |
50±1 | 29000±5000 | 4.5±0.5 | 4 | PVOH | Modified PVAc for wood adhesives, D2 grade, low viscosity | |
50±1 | 58000±10000 | 4.5±0.5 | 4 | PVOH | Modified PVAc for wood adhesives, D2 grade, medium viscosity | |
52±1 | 70000±10000 | 4.5±0.5 | 0 | PVOH | Modified PVAc for wood adhesives, D2 grade, high viscosity | |
54±2 | 43000±10000 | 4.5±0.5 | 0 | PVOH | Plasticized PVAc, medium viscosity | |
52±2 | 80000±10000 | 4.5±0.5 | 0 | PVOH | Plasticized PVAc, high viscosity | |
42±2 | 40000±10000 | 4.5±0.5 | 4 | PVOH | Plasticized PVAc, low solid content |
PRODUCT | WOOD ADHESIVES | PAPER AND CARDBOARD | WOOD LAMINATION | BOOK BINDING | PUTTY AND SEALER | TEXTILE | READY MIX BUILDING COMPOUNDS |
---|---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|---|
55±1 | 9000±2000 | 4.5±0.5 | 5 | CD | High wet scrub resistance | |
55±1 | 3000±1000 | 5.0±0.5 | 13 | CD | High gloss | |
50±1 | 4000±1000 | 4.5±0.5 | 6 | CD | High wet scrub resistance and hiding power | |
50±1 | 4000±1000 | 4.5±0.5 | 3 | CD | High wet scrub resistance | |
50±1 | 7000±1000 | 4.5±0.5 | 3 | CD | High wet scrub resistance | |
50±1 | 7000±1000 | 4.5±0.5 | 5 | CD | Formaldehyde-free, excellent storage stability | |
50±1 | 8000±2000 | 4.5±0.5 | 15 | CD | Formaldehyde and solvents-free | |
50±1 | 3500±500 | 4.5±0.5 | 5 | CD | Very low Formaldehyde content, excellent storage stability |
PRODUCT | INTERIOR MATT PAINTS | EXTERIOR PAINTS | SEMI-GLOSS PAINTS | PUTTY | WALL TEXTURED COATING | HIGH GLOSS PAINTS |
---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|
50±1 | 9000±3000 | 8.5±0.5 | 15 | Styrene/Acrylic | Multi-purpose, high versatility | |
50±1 | 6000±2000 | 8.0±0.5 | 0 | Styrene/Acrylic | Low Tg, good elasticity |
PRODUCT | INTERIOR MATT PAINTS | EXTERIOR PAINTS | SEMI-GLOSS PAINTS | WALL TEXTURED COATING | SILICA PAINTS | WATER PROOF MEMBRANE | READY MIX BUILDING COMPOUNDS |
---|---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Modified PVAc for wood adhesives, D2 grade, low viscosity
Modified PVAc for wood adhesives, D2 grade, medium viscosity
Modified PVAc for wood adhesives, D2 grade, high viscosity
High wet scrub resistance and hiding power
Formaldehyde-free, excellent storage stability
Very low Formaldehyde content, excellent storage stability
Main use |
Possible use