| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
|---|---|---|---|---|---|---|---|
| 60±1 | <1000 | 4.5±1.0 | -30 | S | VA/Acr | High tack and excellent adhesion | |
| 54±1 | 250±150 | 6.0±1.0 | -20 | S | Acr | Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner | |
| 52.5±1.0 | 1000±500 | 4.5±0.5 | -15 | S | VA/Acr | resilient and rubber flooring adhesives, good adhesion on plastic materials | |
| 50±2 | 2000±1000 | 4.5±0.5 | +19 | S | VA/Acr | Shoes adhesives, heat sealable at 65°C | |
| 50±1 | <150 | 6.0±1.0 | -20 | S | Acr | Ready to use product for OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner | |
| 46±1 | <100 | 6.0±1.0 | -20 | S | Acr | Plasticizer free acrylic water-based dispersion characterized by long open time and easy machine cleanability |
| PRODUCT | OPP LAMINATION | FLOORING ADHESIVES | HEAT SEALABLE |
|---|---|---|---|
VINAVIL 2464
|
|
||
|
CRILAT 2823
|
|
||
|
VINAVIL 2416
|
|
||
|
VINAVIL 52 AB
|
|
||
|
CRILAT 2824
|
|
||
|
CRILAT 2825
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
|---|---|---|---|---|---|---|---|
| 50±1 | <500 | 3.5±0.5 | +38 | S | Acr | Alkali soluble | |
| 50±1 | <500 | 3.5±0.5 | +38 | S | Acr | Alkali soluble, high tack | |
| 47±1 | <500 | 4.0±0.5 | +28 | S | Acr | Alkali soluble, IWR |
| PRODUCT | GLASS LABELLING | DIY TRANSPARENT GLUES |
|---|---|---|
| CRILAT 2951 L |
|
|
| CRILAT 2956 L |
|
|
| CRILAT 2954 L |
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | POLYMER TYPE | KEY FEATURES | EMULSIFYING SYSTEM |
|---|---|---|---|---|---|---|
| 66.5±1.5 | 1250±750 | 4.5±0.5 | VA/Acr | Base polymer for self-adhesive compounds, for paper labels or plastic film application, excellent adhesiveness, low cohesion | S | |
| 57±1 | <500 | 5.0±0.5 | Acr | Base polymer for self-adhesive compounds, for paper labels or plastic film application, good adhesiveness, high cohesion | S | |
| 52±1 | 250±150 | 6.5±0.5 | Acr | Excellent adhesion and teck, for general purpose paper labels, ready to use | S | |
| 60±2 | 4500±1000 | 6.0±1.0 | Acr | Excellent adhesiveness on LSE ( Low Surface Energy materials), good shear resistance, ready to use | S | |
| 50±1 | <300 | 7.5±0.5 | Acr | Permanent for decals, excellent adhesiveness on LSE (Low Surface Energy materials), high plasticizers resistance, ready to use | S | |
| 42±1 | 300±100 | 8.0±1.0 | Acr | Designed for self-adhesive sticker industry, ready to use | S |
| PRODUCT | LABELS | LABELS | SPECIAL TAPES | PROTECTIVE FILM | REMOVABLE FILM | PERMANENT ADHESIVES |
|---|---|---|---|---|---|---|
| CRILAT 2440 |
|
|
|
|||
|
CRILAT 2840
|
|
|
|
|||
|
CRILAT P 2703
|
|
|||||
| CRILAT P 2776 |
|
|
||||
| CRILAT P 2727 |
|
|
||||
|
CRILAT P 2744
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 60±2 | 36000±6000 | 5.0±0.5 | 15 | PVOH | High setting speed, high wet tack development, high filler acceptance. | |
| 60±1 | 3000±1000 | 4.5±0.5 | 14 | PVOH | High setting speed, high wet tack development, good workability | |
| 55±1 | 3000±1000 | 4.5±0.5 | 14 | PVOH | Excellent setting speed, outstanding wet tack development, good workability | |
| 50±2 | 48000±6000 | 4.5±0.5 | 14 | PVOH | Fast setting speed, high wet tack development, high loadability with mineral fillers. |
| PRODUCT | PAPER AND CARDBOARD | FAST SETTING TIME | BOOK BINDING | TUBE WINDING | CORRUGATED BOARD | FOLDED BOXES | FURNITURE WOOD ADHESIVE | TOBACCO INDUSTRIES | WOOD VENEERING | WOOD LAMINATION |
|---|---|---|---|---|---|---|---|---|---|---|
| VINAVIL CA/R |
|
|
|
|
|
|
|
|
|
|
| VINAVIL 2160 L |
|
|
|
|
|
|||||
| VINAVIL 2154 L |
|
|
|
|
||||||
| VINAVIL KA/R |
|
|
|
|
|
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 60±1 | 12000±3000 | 5.0±0.5 | 6 | PVOH | High setting time, water resistance | |
| 51±1 | 12000±3000 | 7.0±0.5 | 3 | PVOH | Water resistance, suitable for DIY, fast setting time | |
| 50±1 | 55000±10000 | 4.5±0.5 | 4 | PVOH | Water resistance, high viscosity | |
| 50±1 | 29000±5000 | 4.5±0.5 | 5 | PVOH | Water resistance, medium viscosity | |
| 50±1 | 19000±3000 | 4.5±0.5 | 5 | PVOH | Fast setting time, excellent creep resistance, wood fiber tear | |
| 50±2 | 15000±2000 | 5.0±0.5 | 4 | PVOH | 1K D2 and 2K D4 by addition of inorganic salt, high pot-life | |
| 45±1 | 48000±10000 | 5.0±0.5 | 3 | PVOH | Excellent cost/performance, water resistance |
| PRODUCT | FURNITURE WOOD ADHESIVE | ASSEMBLY | WOOD VENEERING | WOOD LAMINATION |
|---|---|---|---|---|
| VINAVIL 2560 M |
|
|
|
|
|
VINAVIL 2550 FF
|
|
|
|
|
| RAVEMUL M18 |
|
|
|
|
|
RAVEMUL M11
|
|
|
|
|
| VINAVIL 2213 |
|
|
|
|
| VINAVIL 2258 M |
|
|
|
|
| VINAVIL SK |
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 52±1 | 17500±2500 | 3.0±0.2 | 3 | PVOH | High water resistance, excellent creep resistance, high bond strength, heat resistance | |
| 52±1 | 15000±3000 | 3.0±0.2 | 3 | PVOH | Water resistance, high creep resistance, high bond strength, heat resistance | |
| 52±2 | 12000±2000 | 3.0±0.5 | 5 | PVOH | Water resistance, low HCHO content, low discoloration of the glue line | |
| 51.5±1.5 | 13000±3000 | 3.0±0.2 | 3 | PVOH | Water resistance, high creep and heat resistance, suitable for DIY | |
| 50±1 | 10000±2000 | 3.0±0.2 | 3 | PVOH | Water resistance, suitable rheology for industrial applications, good machinability | |
| 57±2 | 15000±3000 | 3.0±0.2 | 8 | PVOH | High solids, water resistance, low HCHO content, no glue line discoloration | |
| 48±1 | 11500±2500 | 4.5±0.5 | 5 | PVOH | Formaldehyde free, high inorganic filler acceptance up to 40 pbw, no metal corrosion, no stains |
| PRODUCT | FURNITURE WOOD ADHESIVE | ASSEMBLY | WOOD VENEERING | WOOD LAMINATION |
|---|---|---|---|---|
| VINAVIL 2252 HV |
|
|
|
|
| VINAVIL 2252 M |
|
|
|
|
| VINAVIL 2253 M |
|
|
|
|
| VINAVIL 2251 L |
|
|
|
|
| VINAVIL 2254 M |
|
|
|
|
| VINAVIL 2257 M |
|
|
|
|
|
VINAVIL 2246 L
|
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | POLYMER TYPE | KEY FEATURES | EMULSIFYING SYSTEM | MFFT °C |
|---|---|---|---|---|---|---|---|
| 52±1 | 7000±3000 | 3.0±0.2 | PVAc | 11% of C14 substitution from BIO SOURCES, water resistance, heat resistance | PVOH | +6 |
| PRODUCT | WOOD LAMINATION / PVC-MDF | FURNITURE WOOD ADHESIVE | ASSEMBLY | WOOD LAMINATION |
|---|---|---|---|---|
| VINAVIL BIO 2211 L |
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 51±2 | 6500±4500 | 3.4±0.4 | 6 | PVOH | 1K, water resistance, low HCHO content, low odor emission, performance stability over time | |
| 48±2 | 7000±3000 | 3.0±0.2 | 6 | PVOH | 1K, water resistance, high bond strength, heat resistance, performance stability over time |
| PRODUCT | FURNITURE WOOD ADHESIVE | ASSEMBLY | WOOD VENEERING | WOOD LAMINATION |
|---|---|---|---|---|
| VINAVIL 2261 L |
|
|
|
|
|
VINAVIL 2256 L
|
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 54±2 | 3000±500 | 5.0±0.5 | 0 | PVOH | Fast setting time, suitable for nozzles and wheel applications | |
| 54±2 | 43000±10000 | 4.5±0.5 | 0 | PVOH | High viscosity | |
| 52±1 | 12500±3500 | 4.5±0.5 | 2 | PVOH | General purpose adhesive for DIY applications | |
| 50±2 | 8500±1500 | 4.5±0.5 | 0 | PVOH | Mosaic glues | |
| 45±2 | 3500±1000 | 4.5±0.5 | 0 | PVOH | Fast setting speed, good workability |
| PRODUCT | PAPER AND CARDBOARD | FAST SETTING TIME | BOOK BINDING | FOLDED BOXES | CASE CLOSING |
|---|---|---|---|---|---|
| RAVEMUL P13 |
|
|
|
|
|
| VINAVIL KA 25 |
|
|
|||
|
VINAVIL MV 15 S
|
|
|
|||
| VINAVIL 2350 L |
|
||||
| VINAVIL P 18 D |
|
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | POLYMER TYPE | KEY FEATURES | EMULSIFYING SYSTEM | MFFT °C |
|---|---|---|---|---|---|---|---|
| 50±2 | 15000±2000 | 5.0±0.5 | PVAc | In combination with VINADUR 500, it is a 2K adhesive for non load bering exteior wood, complying with XT5 durability class according to EN17619 | PVOH | 4 | |
| 48±2 | 7000±3000 | 3.0±0.2 | PVAc | In combination with VINADUR 700, it is a 2K adhesive for non load bearing exterior wood complying with XT6 durability class according to EN17619 | PVOH | 6 | |
| 54±1 | <100 | 2.8±0.3 | - | Hardner based on inorganic salts for wood adhesives in combination with Vinavil 2258 and PW 195 | - | - | |
| 29.5±1 | <100 | 2.9±0.3 | - | Hardner based on inorganic salts for wood adhesives in combination with Vinavil 2258M, XT 500 and PW195 | - | - | |
| - | <300 | - | - | Hardner based on organic polymer for wood adhesives in combination with Vinavil XT 700, D2 and D3 | - | - |
| PRODUCT | FURNITURE WOOD ADHESIVE | ASSEMBLY |
|---|---|---|
| VINAVIL XT 500 |
|
|
|
VINAVIL XT 700
|
|
|
| VINADUR 100 | ||
| VINADUR 500 | ||
| VINADUR 700 |
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | POLYMER TYPE | KEY FEATURES | EMULSIFYING SYSTEM | MFFT °C |
|---|---|---|---|---|---|---|---|
| 50±2 | 15000±2000 | 5.0±0.5 | PVAc | In combination with VINADUR 500, it is a 2k adhesive specifically designed for plywood manufacture | PVOH | 19 |
| PRODUCT | ASSEMBLY |
|---|---|
| VINAVIL PW 195 |
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 60±1 | 11000±4000 | 6.0±0.5 | -27 | S | VAE/Acr terpolymer, excellent balance between adhesion and cohesion | |
| 60±1 | 5500±1500 | 5.0±0.5 | +3 | PVOH | Excellent rheology, good versatility on plastic materials, high setting speed | |
| 60±1 | 4000±1000 | 5.5±1.0 | 7 | PVOH | Good versatility on plastic materials, high setting speed | |
| 55±1 | 8000±2000 | 4.5±0.5 | 3 | PVOH | Good adhesion on plastic materials, good setting speed | |
| 55±1 | 5000±1000 | 5.0±0.5 | +3 | PVOH | Excellent rheology, high wet tack development | |
| 55±2 | <2000 | 4.8±0.8 | +15 | PVOH | Repulpable adhesives | |
| 55±1 | 2500±500 | 5.0±0.5 | +3 | PVOH | Good versatility on plastic materials, excellent rheology and high setting speed | |
| 50±1 | 8000±3000 | 4.5±0.5 | +2 | PVOH | Good adhesion on plastic materials, high viscosity |
| PRODUCT | WOOD LAMINATION / PVC-MDF | 3D VACUUM FORMING | PACKAGING | MOSAIC GLUES | FLOORING ADHESIVES | ADHESIVE PROMOTER | PAPER AND PLASTIC MATERIALS | PAPER CONVERTING | TOBACCO INDUSTRIES | WOOD LAMINATION |
|---|---|---|---|---|---|---|---|---|---|---|
|
VINAVIL 2428
|
|
|
|
|
|
|||||
| VINAVIL EVA 015 |
|
|
|
|
|
|
||||
|
VINAVIL EVA 2607 L
|
|
|
|
|
|
|
|
|||
|
VINAVIL EVA 2601 L
|
|
|
|
|
|
|
||||
| VINAVIL EVA 202 |
|
|
|
|
|
|||||
| VINAVIL EVA 2606 L |
|
|
||||||||
| VINAVIL EVA 2603 L |
|
|
|
|||||||
| VINAVIL EVA 2609 L |
|
|
|
|
| PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | KEY FEATURES |
|---|---|---|---|---|---|---|
| 55±1 | 3000±1000 | 4.5±0.5 | +34 | CD | Heat sealable adhesive without blocking | |
| 50±1 | 1500±1000 | 4.5±0.5 | +30 | S | Heat sealable at 80°C |
| PRODUCT | HEAT SEALABLE |
|---|---|