PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|
60±1 | <1000 | 4.5±1.0 | -30 | S | VA/Acr | High tack and excellent adhesion | |
54±1 | 250±150 | 6.0±1.0 | -20 | S | Acr | Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner | |
52.5±1.0 | 1000±500 | 4.5±0.5 | -15 | S | VA/Acr | resilient and rubber flooring adhesives, good adhesion on plastic materials | |
50±1 | 2000±1000 | 4.5±0.5 | +19 | S | VA/Acr | Heat sealable at 65° C, shoes adhesives | |
50±1 | <150 | 6.0±1.0 | -20 | S | Acr | Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner |
PRODUCT | OPP LAMINATION | FLOORING ADHESIVES | HEAT SEALABLE |
---|---|---|---|
![]() |
![]() |
||
![]() |
![]() |
||
![]() |
![]() |
||
![]() |
![]() |
||
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|
50±1 | <500 | 3.5±0.5 | +38 | S | Acr | Alkali soluble | |
50±1 | <500 | 3.5±0.5 | +38 | S | Acr | Alkali soluble, high tack | |
47±1 | <500 | 4.0±0.5 | +28 | S | Acr | Alkali soluble, IWR |
PRODUCT | GLASS LABELLING | DIY TRANSPARENT GLUES |
---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|
66.5±1.5 | 1250±750 | 4.5±0.5 | -40 | S | VA/Acr | Base polymer for self-adhesive compounds, for paper, labels or plastic film application, excellent adhesiveness, low cohesion | |
57±1 | <500 | 5.0±0.5 | -44 | S | Acr | Base polymer for self-adhesive compounds, for paper labels or plastic film application, good adhesiveness, high cohesion | |
54±1 | 250±150 | 6.0±1.0 | -20 | S | Acr | Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner. Base polymer for self-adhesive for removable tapes, labels and protective films. | |
51±2 | < 250 | 4.5±0.5 | -40 | S | Acr | Self-adhesive for removable tapes and protective film applications | |
60±1 | <1000 | 4.5±1.0 | -30 | S | VA/Acr | High tack and adhesiveness, recommended for specialty tapes applications | |
54±1 | <500 | 7.5±0.5 | -25 | S | Acr | Base polymer for specialty tapes self-adhesive and filmic labels, high film transparency and water whitening resistance (WWR) after water immersion | |
50±1 | <500 | 8.0±1.0 | -25 | S | Acr | Medium adhesion, high cohesion, outstanding PVC plasticizer migration resistance |
PRODUCT | LABELS | OPP LAMINATION | SPECIAL TAPES | PROTECTIVE FILM | REMOVABLE FILM | PERMANENT ADHESIVES |
---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
|||
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|
60±2 | 4500±1000 | 6.0±1.0 | S | Excellent adhesiveness on LSE ( Low Surface Energy materials), good shear resistance | |
50±1 | <300 | 7.5±0.5 | S | Excellent adhesiveness on LSE (Low Surface Energy materials), good shear resistance | |
51±2 | 300±100 | 8.0±0.5 | S | Removable self-adhesive, low adhesiveness, high cohesion | |
52±2 | <250 | 7.0±1.0 | S | Specifically designed for wine label applications | |
42±1 | 300±100 | 8.0±1.0 | S | Designed for self-adhesive sticker industry |
PRODUCT | LABELS | SPECIAL TAPES | PROTECTIVE FILM | REMOVABLE FILM | PERMANENT ADHESIVES |
---|---|---|---|---|---|
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
|||
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|
50±1 | 2000±1000 | 8.0±1.0 | S | Sty/Acr | Medium hard hand, good flexibility | ||
49±1 | <200 | 8.0±0.5 | -15 | S | Acr | Self-crosslinkable at RT, soft hand | |
46±1 | <1000 | 9.0±0.5 | +26 | S | Acr | Self-crosslinkable at RT, stiff hand | |
45±1 | <400 | 4.0±0.5 | +48 | S | VA/Acr | Good water and solvent resistance | |
45±1 | <400 | 3.0±0.5 | +35 | S | VA/Acr | Water and solvent resistance | |
44±1 | <1000 | 3.3±0.5 | -10 | S | VA/Acr | Self-crosslinkable at 140°C, low HCHO | |
42±2 | <100 | 3.5±0.5 | -15 | S | Acr | Cationic resin, soft hand |
PRODUCT | NON WOVEN / ABRASIVE FIBERS | WADDING / NON WOVEN | TEXTILE PRINTING | FLOCKING |
---|---|---|---|---|
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
PARTICLE SIZE DISTRIBUTION µm |
MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|---|
55±1 | 1000±500 | 4.5±0.5 | +25 | 0.3±0.1 | 7 | VA/Acr | High abrasion resistance | |
50±1 | 9000±3000 | 7.5±0.5 | +24 | 0.11±0.03 | 16 | Sty/Acr | Multi-purpose, odourless | |
50±1 | 9000±3000 | 8.5±0.5 | +24 | 0.11±0.03 | 15 | Sty/Acr | High versatile, multi-purpose | |
50±1 | 2500±1000 | 7.5±0.5 | +26 | 0.11±0.03 | 15 | Sty/Acr | High versatile, multi-purpose | |
50±1 | 2000±1000 | 8.0±0.5 | +10 | 0.11±0.03 | 5 | Sty/Acr | Odourless, low VOC, high weathering resistance | |
50±1 | 2500±1000 | 7.5±0.5 | +2 | 0.11±0.03 | 0 | Sty/Acr | High water barrier, high weathering resistance | |
50±1 | 6000±2000 | 8.0±0.5 | +6 | 0.11±0.03 | 0 | Sty/Acr | High alkali resistance | |
50±1 | < 1000 | 8.0±0.5 | +8 | 0.09±0.03 | 0 | Acr | No coalescing required, low VOC, high weathering resistance | |
47±1 | < 200 | 7.75±0.75 | +18 | 0.15±0.05 | 10 | Acr | High color retention, high weathering resistance | |
48±1 | < 300 | 8.0±0.5 | +21 | 0.15±0.05 | 10 | Acr | High water resistance, high weathering resistance | |
46±1 | 4000±1500 | 8.0±1.0 | +18 | 0.15±0.05 | 9 | Acr | Decorative paints, good rheological properties |
PRODUCT | INDOOR PAINTS | OUTDOOR PAINTS | TEXTURED COATINGS | HIGH GLOSS PAINTS | SILICA PAINTS AND TEXTURED COATING |
---|---|---|---|---|---|
![]() |
![]() |
![]() |
|||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
PARTICLE SIZE DISTRIBUTION µm |
MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|---|
47±1 | < 600 | 9.5±0.5 | 3 | 0.17±0.03 | 0 | Acr | Excellent mechanical properties, abrasion resistance | |
49±1 | 1250±750 | 7.0±0.5 | +24 | 0.11±0.03 | 17 | Sty/Acr | Paste adhesives, high adhesion, water resistance | |
50±1 | 9000±3000 | 8.5±0.5 | +24 | 0.11±0.03 | 15 | Sty/Acr | Multi-purpose, high versatility | |
50±1 | 2500±1000 | 7.5±0.5 | +2 | 0.11±0.03 | 0 | Sty/Acr | High water barrier | |
49.5±1.0 | 3000±1000 | 7.0±0.5 | -3 | 0.13±0.03 | 0 | Sty/Acr | High adhesion, low water absorption | |
55.5±1.0 | < 1000 | 7.4±0.6 | -6 | 0.35±0.05 | 0 | Sty/Acr | High flexibility at low temperature | |
52.5±1.0 | 1000±500 | 7.0±0.5 | -10 | 0.14±0.02 | 0 | Sty/Acr | Good flexibility in combination with cement | |
52.5±1.0 | < 600 | 6.5±0.5 | -35 | 0.17±0.04 | 0 | Sty/Acr | Good flexibility in combination with cement |
PRODUCT | PRIMER | TILE ADHESIVES | READY MIX BUILDING COMPOUNDS | WATER PROOF MEMBRANES mono-component | WATER PROOF MEMBRANES bi-components |
---|---|---|---|---|---|
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
||||
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
PARTICLE SIZE DISTRIBUTION µm |
MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|---|
46±1 | < 1000 | 9.0±0.5 | - | 0.09±0.03 | 11 | Acr | High gloss, good rheology in application, good weathering resistance | |
44±1 | < 300 | 8.0±0.5 | - | 0.04±0.02 | 11 °C | Acr | High blocking resistance | |
44±1 | < 300 | 8.0±0.5 | - | 0.04±0.02 | 0 | Acr | Good flexibility | |
45±1 | < 200 | 8.0±0.5 | +40 | 0.10±0.02 | 40 | Acr | Good hardness, stain resistance | |
45±1 | < 200 | 8.0±0.5 | +50 | 0.09±0.03 | 48 | Sty/Acr | Excellent adhesion to metals, anti-corrosion properties | |
31±1 | < 100 | 7.0±1.0 | +15 | 0.03±0.01 | 5 | Acr | High consolidating effect | |
28±1 | < 100 | 4.0±1.0 | +19 | 0.06±0.01 | 5 | Acr | Cationic emulsifying system |
PRODUCT | INDOOR ANTI-STAINS PAINTS | PRIMER NANO SIZE | OUTDOOR WOOD COATING | INDOOR WOOD COATING | WOOD IMPREGNATING | DIRECT TO METAL | METAL BASE COAT | HIGH GLOSS ENAMEL |
---|---|---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
||||||
![]() |
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
High tack and excellent adhesion
Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner
resilient and rubber flooring adhesives, good adhesion on plastic materials
Heat sealable at 65° C, shoes adhesives
Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner
Alkali soluble
Alkali soluble, high tack
Alkali soluble, IWR
Base polymer for self-adhesive compounds, for paper, labels or plastic film application, excellent adhesiveness, low cohesion
Base polymer for self-adhesive compounds, for paper labels or plastic film application, good adhesiveness, high cohesion
Excellent for dry OPP lamination, 48 hours stability after the addition of aliphatic isocyanate hardner. Base polymer for self-adhesive for removable tapes, labels and protective films.
Self-adhesive for removable tapes and protective film applications
High tack and adhesiveness, recommended for specialty tapes applications
Base polymer for specialty tapes self-adhesive and filmic labels, high film transparency and water whitening resistance (WWR) after water immersion
Medium adhesion, high cohesion, outstanding PVC plasticizer migration resistance
Excellent adhesiveness on LSE ( Low Surface Energy materials), good shear resistance
Excellent adhesiveness on LSE (Low Surface Energy materials), good shear resistance
Removable self-adhesive, low adhesiveness, high cohesion
Specifically designed for wine label applications
Designed for self-adhesive sticker industry
Medium hard hand, good flexibility
Self-crosslinkable at RT, soft hand
Self-crosslinkable at RT, stiff hand
Good water and solvent resistance
Water and solvent resistance
Self-crosslinkable at 140°C, low HCHO
Cationic resin, soft hand
High abrasion resistance
Multi-purpose, odourless
High versatile, multi-purpose
High versatile, multi-purpose
Odourless, low VOC, high weathering resistance
High water barrier, high weathering resistance
High alkali resistance
No coalescing required, low VOC, high weathering resistance
High color retention, high weathering resistance
High water resistance, high weathering resistance
Decorative paints, good rheological properties
Excellent mechanical properties, abrasion resistance
Paste adhesives, high adhesion, water resistance
Multi-purpose, high versatility
High water barrier
High adhesion, low water absorption
High flexibility at low temperature
Good flexibility in combination with cement
Good flexibility in combination with cement
High gloss, good rheology in application, good weathering resistance
High blocking resistance
Good flexibility
Good hardness, stain resistance
Excellent adhesion to metals, anti-corrosion properties
Cationic emulsifying system
Main use |
Possible use