PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|---|
60±1 | 11000±4000 | 6.0±0.5 | -27 | S | VAE/Acr terpolymer, excellent balance between adhesion and cohesion | |
60±1 | 5500±1500 | 5.0±0.5 | +3 | PVOH | Excellent rheology, high cold resistance in wood lamination | |
60±1 | 4500±1000 | 5.0±0.5 | +7 | PVOH | High PU compatibility | |
60±1 | 4000±1000 | 6.5±0.5 | +7 | PVOH | High creep resistance in wood lamination and in PVC/ paper application | |
55±1 | 5000±1000 | 5.0±0.5 | +3 | PVOH | Excellent rheology, high wet tack development | |
55±2 | <2000 | 4.75±0.75 | +15 | PVOH | Repulpable adhesives | |
55±1 | 2500±500 | 5.0±0.5 | +3 | PVOH | Good versatility on plastic materials, excellent rheology and high setting time | |
50±1 | 8000±3000 | 4.5±0.5 | +2 | PVOH | Good adhesion on plastic materials, high viscosity |
PRODUCT | WOOD LAMINATION / PVC-MDF | 3D VACUUM FORMING | PACKAGING | MOSAIC GLUES | FLOORING ADHESIVES | ADHESIVE PROMOTER | PAPER AND PLASTIC MATERIALS | PAPER CONVERTING | TOBACCO INDUSTRIES |
---|---|---|---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
![]() |
|||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
||||
![]() |
![]() |
![]() |
|||||||
![]() |
![]() |
![]() |
![]() |
||||||
![]() |
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|---|
50±1 | 2000±1000 | 5.75±0.75 | +15 | PVOH | Good balance between elongation and fiber toughness | |
50±1 | <900 | 4.5±0.5 | -10 | S | Very soft hand, self-crosslinkable | |
50±2 | 500±200 | 5.0±0.5 | +3 | PVOH | Flocking on PS substrates | |
46±1 | <600 | 3.25±0.25 | - | S | Medium hard hand, self-crosslinkable |
PRODUCT | NON WOVEN | TEXTILE PRINTING | FLOCKING | CARPET BACKING |
---|---|---|---|---|
![]() |
![]() |
![]() |
||
![]() |
![]() |
![]() |
||
![]() |
![]() |
|||
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | MFFT °C |
EMULSIFYING SYSTEM | KEY FEATURES |
---|---|---|---|---|---|---|
52±1 | 3500±1000 | 4.5±0.5 | 0 | CD | Odourless paints, very low VOC | |
50±1 | 2000±1000 | 5.8±0.8 | 2 | PVOH | High alkali and chemical resistance |
PRODUCT | INDOOR PAINTS | OUTDOOR PAINTS | TEXTURED COATINGS | THERMAL INSULATION SYSTEM (EIFS) | INTUMESCENT PAINTS | LOW VOC PAINTS |
---|---|---|---|---|---|---|
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
![]() |
![]() |
![]() |
![]() |
![]() |
VAE/Acr terpolymer, excellent balance between adhesion and cohesion
Excellent rheology, high cold resistance in wood lamination
High PU compatibility
High creep resistance in wood lamination and in PVC/ paper application
Excellent rheology, high wet tack development
Repulpable adhesives
Good versatility on plastic materials, excellent rheology and high setting time
Good adhesion on plastic materials, high viscosity
Good balance between elongation and fiber toughness
Very soft hand, self-crosslinkable
Flocking on PS substrates
Medium hard hand, self-crosslinkable
Odourless paints, very low VOC
High alkali and chemical resistance
Main use |
Possible use