PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
PARTICLE SIZE DISTRIBUTION µm |
MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|---|
47±1 | < 600 | 9.0±1.0 | 3 | 0.17±0.03 | 0 | Acr | Excellent mechanical properties, abrasion resistance | |
49±1 | 1550±500 | 7.0±0.5 | +24 | 0.11±0.03 | 17 | Sty/Acr | Paste adhesives, high adhesion, water resistance | |
50±1 | 9000±3000 | 8.5±0.5 | +24 | 0.11±0.03 | 15 | Sty/Acr | Multi-purpose, high versatility | |
50±1 | 2500±1000 | 7.5±0.5 | +2 | 0.11±0.03 | 0 | Sty/Acr | High water barrier | |
49.5±1.0 | 3000±1000 | 7.0±0.5 | -3 | 0.13±0.03 | 0 | Sty/Acr | High adhesion, low water absorption | |
55.5±1.0 | < 1000 | 7.2±0.8 | -6 | 0.35±0.05 | 0 | Sty/Acr | High flexibility at low temperature | |
52.5±1.0 | 1000±500 | 7.0±0.5 | -10 | 0.14±0.02 | 0 | Sty/Acr | Good flexibility in combination with cement | |
52.5±1.0 | < 600 | 6.5±0.5 | -35 | 0.17±0.04 | 0 | Sty/Acr | Good flexibility in combination with cement |
PRODUCT | PRIMER | TILE ADHESIVES | READY MIX BUILDING COMPOUNDS | WATER PROOF MEMBRANES mono-component | WATER PROOF MEMBRANES bi-components |
---|---|---|---|---|---|
CRILAT 4803
![]() |
![]() |
||||
CRILAT 4723
![]() ![]() |
![]() |
![]() |
![]() |
||
CRILAT 4724 |
![]() |
![]() |
![]() |
||
CRILAT 4768
![]() |
![]() |
||||
CRILAT 4703
![]() ![]() |
![]() |
||||
CRILAT 4707 |
![]() |
![]() |
![]() |
||
CRILAT 4712
![]() |
![]() |
![]() |
![]() |
||
CRILAT 4736
![]() |
![]() |
![]() |
PRODUCT | SOLID CONTENT % |
VISCOSITY mPa*s |
pH | Tg °C |
PARTICLE SIZE DISTRIBUTION µm |
MFFT °C |
POLYMER TYPE | KEY FEATURES |
---|---|---|---|---|---|---|---|---|
31±1 | < 100 | 7.0±1.0 | +15 | 0.03±0.01 | 5 | Acr | High consolidating effect | |
28±1 | < 100 | 4.0±1.0 | +19 | 0.06±0.01 | 5 | Acr | Cationic emulsifying system |
PRODUCT | INDOOR ANTI-STAINS PAINTS | PRIMER NANO SIZE | WOOD IMPREGNATING |
---|---|---|---|
CRILAT 4815
![]() |
![]() |
![]() |
![]() |
CRILAT 4896
![]() ![]() |
![]() |
![]() |
![]() |
PRODUCT | POLYMER TYPE | ASH CONTENT | Tg °C |
MFFT °C |
KEY FEATURES |
---|---|---|---|---|---|
VA/VV | 11.5±1.5 | +28 | 15 | High tensile strength | |
VA/Acr/VV | 11.5±1.5 | +16 | 5 | Medium flexibility | |
VAE | 11.5±1.5 | +15 | 0 | Good flexibility | |
VAE | 11.5±1.5 | -3 | 0 | High flexibility | |
VAE | 11.5±1.5 | -6 | 0 | High flexibility | |
VA/VV | 11.5±1.5 | +33 | 16 | Self-levelling | |
VAE | 11.5±1.5 | -5 | 0 | Hydrophobic, flexible |
PRODUCT | TILE ADHESIVES | FLEXIBLE COMPOUNDS | PLASTERS WALL TEXTURED COATINGS | HYDROPHOBIC COMPOUNDS | SELF LEVELLING COMPOUNDS | THERMAL INSULATION SYSTEM (EIFS) |
---|---|---|---|---|---|---|
VINAVIL 5526 |
![]() |
|||||
VINAVIL 5406 P |
![]() |
![]() |
![]() |
![]() |
||
VINAVIL E06 PA |
![]() |
![]() |
![]() |
![]() |
![]() |
|
VINAVIL 5603 P
![]() |
![]() |
![]() |
![]() |
|||
VINAVIL 5603 PB
![]() |
![]() |
![]() |
![]() |
|||
VINAVIL SL11 P |
![]() |
|||||
VINAVIL 5605 HP
![]() |
![]() |
![]() |
![]() |
PRODUCT | K VALUE | SOFTENING POINT °C |
POLYMER TYPE |
---|---|---|---|
40±2 | 83÷101 | PVAc | |
50±3 | 100÷119 | PVAc | |
62±3 | 145÷165 | PVAc | |
118±5 | - | PVAc | |
43±2 | - | VA/CR | |
50±1 | - | VA/CR | |
30±2 | - | VA/CR |
PRODUCT | WOOD PASTE | HOBBY SOLVENT GLUE | PARQUET SOLVENT BASED ADHESIVES | SOUND DUMPING PANELS | HEAT SEALABLE AND EXTRUDABLE ADHESIVES | COMPOSITE MATERIAL ADDITIVES | SOLVENT BASED INKS | IWR PROMOTER IN COMBINATION WITH CRILAT 2951 L | HIGH BONDING SOLVENT BASED ADHESIVES |
---|---|---|---|---|---|---|---|---|---|
VINAVIL K 40 |
![]() |
![]() |
![]() |
||||||
VINAVIL K 50 |
![]() |
![]() |
![]() |
![]() |
|||||
VINAVIL K 60 |
![]() |
![]() |
![]() |
||||||
VINAVIL K 115 |
![]() |
![]() |
|||||||
VINAFLEX CR 25 |
![]() |
||||||||
VINAFLEX CR 50 |
![]() |
||||||||
VINAFLEX CR 95 |
![]() |
Main use |
Possible use